Brominated reactive flame retardant vinyl ester resins, such as 905-2, 905-2HOI, 905-N, 915, CHEMPULSE 915-HOI, etc., have good corrosion resistance. At the same time, due to the introduction of halogen into the resin system, it has excellent flame retardant properties, and is mainly used in corrosion-resistant equipment with flame retardant requirements.
Among them, 905 series is mainly used in the preparation of FRP chimney in large coal-fired power plant because of its excellent comprehensive performance in corrosion resistance, fire resistance, good mechanical performance, stable performance and good operability. 915 series is widely used in the preparation of anode tube and shell in wet dust collector because of its excellent corrosion resistance, flame resistance and self-extinguishing property.
Performance | 905-2 | 905-2HOI | 905-N | 915 | CHEMPULSE 915-HOI |
Solid Content %) | 58±1.5 | 58±1.5 | 62±1.5 | 54±1 | 55±2 |
*1 Viscosity(cps) | 380±100 | 380±100 | 350±100 | 350±100 | 300±50 |
Proportion (Kg/L) | 1.15±0.02 | 1.15±0.02 | 1.15±0.01 | 1.06±0.01 | 1.09±0.01 |
*2 Gel Time (min) | 20±5 | 20±5 | 20±5 | 15±5 | 17.5±7.5 |
Quality Guarantee Period (month,25℃) | 6 | 6 | 3 | 6 | 6 |
*1 LVT#3-60rpm,25℃
*2 55%MEKP:1.2%,6% cobalt caproate:0.4%,100%DMA:0.05%,25℃
Performance | 905-2 | 905-2HOI | 905-N | 915 | CHEMPULSE 915-HOI | Test Method |
Tensile Strength(MPa) | 76-90 | 76-90 | 68-82 | 75-85 | 76-84 | ISO 527-2 \GB/T 2567 |
Tensile Modulus(GPa) | 3.4-3.7 | 3.4-3.7 | 3.4-3.6 | 2.9-3.2 | 3.0-3.4 | ISO 527-2 \GB/T 2567 |
Elongation(%) | 4.5-5.5 | 4.5-5.5 | 5.2-5.7 | 5.0-7.0 | 4.0-7.0 | ISO 527-2 \GB/T 2567 |
Flexural Strength(MPa) | 111-132 | 111-132 | 122-136 | 115-135 | 131-142 | ISO 178 \GB/T 2567 |
Flexural Modulus(GPa) | 3.5-3.8 | 3.5-3.8 | 3.5-3.8 | 3.1-3.4 | 3.2-3.6 | ISO 178 \GB/T 2567 |
HDT(℃) | 102-108 | 102-108 | 130-136 | 84-90 | 80-85 | ISO 75 \GB/T 1634 |
Hardness (Barcol) | 35-40 | 35-40 | 39-45 | 33-37 | 35-40 | GB/T 3854 |
Oxygen Index | 25-28 | 28-32 | 25-28 | 28-32 | 32-35 | ISO 4589-2 \GB/T 2406 |